1200G High Silica Cloth Fabric 1.3mm Satin Weave Fiberglass Cloth For Fire Blank



Products Visitors:452
Products description:


1200G High Silica Fabric 1.3mm Satin Weave Fiberglass Cloth For Fire Blanket


High silica fabric is inorganic fiberglass fabric with more than 96% SiO2 content. The post treatments make the 850g/m2 e-glass fiberglass fabric into 600g/m2. Except for SiO2, the acid treatment and calcination improve the fiberglass fabric and make it with higher softening point and higher density. Softening point of 1200g high silica fabric is close to 1700℃. And it can be used at 1200℃ continuously. High silica fabric is a high tensile strength, durable, high temperature material with stable physical/chemical properties. It is always used for fire, welding blanket and thermal insulation sealing application.


This high silica cloth is woven in satin weaving. Standard widths are 91.44cm and 100cm. Colors are white or brown.


Specification:


Items High Silica Cloth
Weight 1200g/m2 ± 30
Thickness 1.3mm±0.05
Weaving Satin
Width 91.44cm, 100cm
Temperature ≤1200°C


Features:


  1. 96% SiO2 content
  2. Thermal insulation
  3. High density
  4. No hot loss, stable
  5. Anti chemical agents
  6. Heavy duty
  7. Abrasion resistance


Applications:


  • Welding, fire blanket
  • Elecrtrical insulation cover, switch box
  • Car, rocket, missile, spacecraft fields
  • Heat insulation sealing in hot tunnel and glass kiln



Specification

 

 

Weight

18oz

36oz

Thickness

0.6mm

1.4mm

SIO2 content

90%min

96%min

Burn loss

3.0%max

3.0%max

Working temperature

1800℉ (982℃)

1800℉ (982℃)

Instantaneous temperature

3000℉(1649℃)

3000℉(1649℃)

15 minute temperature

2500℉(1371℃)

2500℉(1371℃)